Physical
Properties |
Typical Values |
ASTM Method |
| IZOD Impact Strength |
| Notched at 73°F (22.78°C) |
2.5 ft lbs/in |
D-256 |
| Tensile Strength |
| To break |
5,400 psi |
D-638 |
| Elongation before break |
70% |
D-638 |
| Flexural Strength |
| Loan to stretch outer surface 5% |
9,200 psi |
D-790 |
| Specific Gravity |
1.04 |
D-792 |
| Rockwell Hardness |
R102 |
D-785 |
| Deflection Temperature |
| Temperature at which material deflects .010" (.254mm)
at 264 psi |
175°F (79.44°C) |
D-648 |
| Coefficient of Thermal Expansion |
| Inch/inch/°F |
5.0 x
10-5 |
D-696 |
| Vicat Softening Point |
|
|
| Temperature for needle to penetrate 1mm
(90°F/hr, 2.2 lbs) |
225°F (107.22°C) |
D-1525 |
|
| The physical properties of the MATTES engraving material are largely controlled
by the base material. This material was chosen to provide a good balance of properties
for this product to satisfy a wide range of uses. |
| The material softens at about 200°F (93.00°C) sufficiently so that it can be bent
where needed. It can be drilled, sawed, sheared, nailed, bonded and die-cut. |
| The base material, as well as the foils, were tested for flammability by Underwriters
Laboratories. The base material is rated as 94 HB on the UL 94 test. The foil was judged
as not contributing to combustion of the base. |
| Most of the colors will exhibit slight fading under prolonged exposure to direct
sunlight. There are, however, those which tend to fade more severely. This material
is designed for use where no direct extreme exposure is encountered. |
| NOTE: The above information is given in good faith, but no warranty,
express or implied, is given. |